牌号L-1225Y厂家(产地)日本帝人用途级别注塑级原料技术数据性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水率24hr，in23℃ASTMD-5700.20%物理性能比重ASTMD-7921.20阻燃性厚度1.47mmUL9494V-2透光率厚度3mmASTMD-100388%折射率ASTMD-5421.585阻燃性厚度3.05mmUL9494V-2机械性能耐冲击强度值艾氏、带缺口厚度3.2mmASTMD-256830(85)j/m(kgf.cm/cm)弯曲强度ASTMD-79090(920)Mpa(kgf/cm2)拉伸率屈服点ASTMD-6386断裂点ASTMD-638140拉伸强度屈服点ASTMD-63862(630)Mpa(kgf/cm2)断裂点ASTMD-63878(800)Mpa(kgf/cm2)洛氏硬度ASTMD-78577洛氏硬度耐冲击强度值艾氏、带缺口厚度6.4mmASTMD-256130(13)j/m(kgf.cm/cm)弯曲模量ASTMD-7922260(23000)Mpa(kgf/cm2)拉伸模量ASTMD-6382130(21700)Mpa(kgf/cm2)压缩强度ASTMD-69576(780)Mpa(kgf/cm2)电气性能体积电阻率ASTMD-25731016 .cm耐导电径迹性（CTI）IEC112300V介电率106HzASTMD-1502.9介电率60HzASTMD-1502.95介电正切106HzASTMD-1500.009耐电弧性ASTMD-495110sec介电正切60HzASTMD-1500.0004绝缘破坏强度快速加压值厚度1.6mmASTMD-14930KV/mm加工性能成型收缩率流动方向ASTMD-9550.5～0.7%垂直方向ASTMD-9550.5～0.7%热性能负荷挠曲温度负荷0.451MPa(4.6kgf/cm)ASTMD-648142 C线膨胀系数流动方向ASTMD-696710-5cm/cm/℃垂直方向ASTMD-696710-5cm/cm/℃负荷挠曲温度负荷1.813MPa(18.6kgf/cm)ASTMD-648132 C温度指数电学式厚度1.47mmUL746B125 C冲击式厚度1.47mmUL746B115 C非冲击式厚度1.47mmUL746B125 C