玛拉胶带Acrylic Polyethylene terephthalate film tape
产品描述PRODUCT DI
KingDays KD312 is polyethylene terephthalate film, single coated with a acrylic adhesive.
|
项目 |
参数 |
||
|
颜色Color |
淡黄、深黄、蓝色、红色、绿色、黑色、白色、透明、半透明 |
||
|
带基厚度Backing thickness |
0.02mm |
0.025mm |
0.05mm |
|
总厚度Total thickness |
0.035mm±0.003 |
0.06mm±0.003 |
0.08mm±0.003(GB7125) |
|
宽度公差Width tolerance |
±0.2mm |
||
|
胶芯内径Core inner diameter |
76mm±1 |
||
|
成份Element |
聚酯薄膜PET，丙烯酸丁酯BA，丙烯酸异辛酯Z-EHA，醋酸乙酯EAC，进口颜料，无卤阻燃?? |
||
|
胶型Adhesive |
Acrylic丙烯酸 |
||
|
抗张强度Tensile strength |
3.0KN/m |
3.30KN/m |
|
|
断裂伸长率Elongation (at break) |
35% |
40% |
|
|
对钢板粘性Adhesive to steel |
3.1 N/10mm |
3.5N/10mm |
|
|
剥离强度Peeledstrength |
≥250N/M |
≥300N/M |
|
|
介电强度Dielectric strength |
≥3.5KV |
≥4.20KV (GB7125-87) |
|
|
绝缘电阻Insulation resistance |
1.0x106欧 |
||
|
电解腐蚀系数 Electrolytic corrosion factor |
≥0.9 |
||
|
温度Temperature Class |
-40℃~150℃ |
||
|
着火点Kindling temperature |
>200℃ |
||
|
阻燃级别Flame retardant |
UL94V0 |
||
|
相对电痕指数物料组合 CTI Material group |
600 |
||
|
未固化（浸于甲苯溶液5分钟） No solidify |
无 |
||
|
耐溶性Endurance dissolvent |
特级胶带耐任何化学溶剂，1级耐二甲苯、醋酸乙酯 |
||
|
耐候性Endurance weather |
根据UL510标准存放100小时保持胶带不变 |
||
|
库存条??Deposited qualification |
温度25℃，湿度70%RH |
||
|
库存有效时间 Deposited period of validity |
温度-35℃~40℃、湿度≤80%时，可保存1~2年。常温1年 |
||
|
应用范围Be used for |
各种电机、变压器等特殊部分的绝缘保护，线圈缠绕固定等 |
||
安全注意事项?杭尤群螅哂?150℃时，有蒸气放出，对眼与呼吸道有一定的刺激。皮肤与胶面频繁接触后，虽无害亦需用清水洗去。勿高温（≥130℃）烘烤和置于强酸、强碱内。高温有害分解物CO、CO2。胶带使用完，塑料内芯可回收利用，废弃胶带尾料应集中处理，勿燃烧。
颜色：多种。
主要成份：PET、氩克力胶（或橡胶）。
耐温：130℃。
耐压：4.5kV。
特性：阻燃。
用途：B级变压器的层间绝缘、外包扎，复印机、打印机粘贴等。
产地：美国（3M公司,Permacel公司）、日本寺冈（Teraoka）、苏州。
型号：1350F,1318,5,35,630F,P-256,JY312。