PPS 日本东丽 AR10MB 物性认证数据表数据提供企业： 性能项目测试条件测试方法数值/描述单位机械性能拉伸强度(引张强度)ASTM D638/ISO 527140kg/cm (MPa)[Lb/in2]断裂伸长率ASTM D638/ISO 5270.7%拉伸模量ASTM D638/ISO 527kg/cm (MPa)[Lb/in2]拉伸屈服伸长率(延伸率)ASTM D638/ISO 527%拉伸断裂伸长率(延伸率)ASTM D638/ISO 527%弯曲模量(弯曲弹性率)ASTM D790/ISO 17822.5kg/cm (MPa)[Lb/in2]弯曲强度ASTM D790/ISO 178165kg/cm (MPa)[Lb/in2]洛氏硬度ASTM D785122IZOD 缺口冲击强度1/4\" 23℃ASTM D256/ISO 179kg cm/cm(J/M)ft lb/in1/4\" -30℃ASTM D256/ISO 179kg cm/cm(J/M)ft lb/in1/8\" 23℃ASTM D256/ISO 179kg cm/cm(J/M)ft lb/in1/8\" -30℃ASTM D256/ISO 179kg cm/cm(J/M)ft lb/inCharpy冲击强度23℃ （缺口）ASTM D256/ISO 1795kg cm/cm(J/M)ft lb/in-30℃（缺口）ASTM D256/ISO 179kg cm/cm(J/M)ft lb/in23℃（无缺口）ASTM D256/ISO 17911kg cm/cm(J/M)ft lb/in-30℃（无缺口）ASTM D256/ISO 179kg cm/cm(J/M)ft lb/in物性性能比重（密度）ASTM D792/ISO 11831.96成型收缩率ASTM D9550.2%熔融指数（流动系数）200℃/5kgASTM D1238/ISO 1133g/10min220℃/10kgASTM D1238/ISO 1133g/10min吸水率 23℃/24HASTM D570/ISO 620.02%热性能热变形温度退火ASTM D648/ISO 75 260℃（℉）未退火ASTM D648/ISO 75℃（℉）维卡软化点ASTM D1525/ISO R306℃（℉）熔点-278℃（℉）燃烧性（率）UL94V-0线性膨胀系数ASTM D696/ISO 113591.6mm/mm.℃电气性能介电常数100HZASTM D150/IEC 602504.31MHZASTM D150/IEC 60250体积电阻率ASTM D257/IEC 600931014 .cm表面电阻率ASTM D257/IEC 60093 耐电弧性ISO 14782加工条件干燥条件加工温度射嘴℃料筒前段℃料筒中段℃料筒后段℃熔体温度℃模具温度℃压力注塑压力Mpa保压压力Mpa背压Mpa螺杆转速rpm其他备注颜色本色，黑特性用途