型高温煅烧氧化铝Alpha High temperature calcined alumina极好的高温增磨剂。It is excellent high temperature increase grinding.技术指标:Technical indices:(1)比重:3.9g/cm3 (1) Density: 3.9g/cm3(2)松散密度:105-130ml/100g (2) Porosity: 105-130ml/100g(3)震实刻度:55-77 ml/100g (3) Tap density: 55-77 ml/100g(4)粒度筛分:325目 (4) Granularity Screening:325mm(5)粒子尺寸:2.8 m (5) Particle size: 2.8 m(6)挥发份: 0.1% (6) Volatile: 0.1%(7)800℃灼烧损失:0.1% (7) residue on ignition 800℃: 0.1%(8) Al2O3含量: 99.5% (8) Al2O3 content: 99.5%(9) - Al2O3含量: 94% (9) - Al2O3 content: 94%